Austenitic · Stainless Steel
304L Low-Carbon Austenitic Stainless Steel
Chemical composition and mechanical properties per ASTM A240; available sizes are standard ranges.
① Chemical Composition (ASTM A240, %)
| Element | Range |
|---|---|
| C | ≤0.03 |
| Si | ≤0.75 |
| Mn | ≤2.00 |
| P | ≤0.045 |
| S | ≤0.030 |
| Cr | 18.0–20.0 |
| Ni | 8.0–12.0 |
② Mechanical Properties (ASTM A240)
| Property | Requirement |
|---|---|
| Tensile Strength Rm | ≥ 485 MPa |
| Yield Strength Rp0.2 | ≥ 170 MPa |
| Elongation A | ≥ 40% |
| Hardness | ≤ 201 HBW |
③ Available Sizes (Standard Range)
- Thickness: 0.3–60 mm
- Width: ≤ 2000 mm
- Form: coil / sheet / plate / circle / cut strip on request
- Surface: 2B · BA · No.1 · No.4 · HL · 8K on request
④ Applicable Standards
ASTM A240 · EN 10088-2 · JIS G4304/4305 · GB/T 3280
⑤ Typical Applications
Thick-wall welded parts, large tanks, chemical equipment, piping, welded assemblies without post-weld heat treatment
⑥ Substitution and Selection Tips
Slightly lower strength than 304 but better intergranular corrosion resistance after welding. If solution annealing is applied after welding, 304 is sufficient.
Chemical and mechanical data cited from the public ASTM A240 standard. Available sizes are standard ranges; the contract and technical agreement shall prevail.